Shock fracture mechanisms of different scales were investigated on epoxy composite materials reinforced with silicon carbide microparticles of different concentrations. It is shown that the high heterogeneity of the epoxy composites at different structural scales is one of the factors responsible for their physical and mechanical properties. Under dynamic loading, the material reveals a developed structural scale hierarchy which provides self-consistent deformation and fracture of the material bulk with the lead of rotational deformation modes. As a result, microcracks develop due to low shear strain limited in addition by reinforcing particles. At the start of a main crack, microscale mechanisms dominate, whereas the propagation of its front is governed by macroscale fracture mechanisms.

Изучено влияние напряженного состояния границ раздела структурных элементов блочной среды на ее деформационный отклик при динамических воздействиях. Показано, что приведенная величина сдвигового напряжения и среднее напряжение являются основными факторами, определяющими деформационный отклик границы раздела. Для аналитического описания зависимости величины инициированного необратимого смещения на границе от приведенного сдвигового напряжения предложено использовать логистическую функцию, центральная точка которой соответствует переходу от квазиупругой к квазипластической стадии сдвигового деформирования межблочной границы. Показана значимость полученных эмпирических зависимостей для понимания закономерностей накопления необратимых деформаций во фрагментах разломных зон и, в частности, для развития предложенного ранее авторами подхода к оценке характерного уровня действующих сдвиговых напряжений на отдельных участках тектонических разломов.

The paper studies the phase composition, microstructure, and mechanisms of plastic deformation and fracture under impact load in a laminate obtained by pressure welding of VT6 titanium alloy sheets. Under impact loading at 20 and -196°C, the material is delaminated into sheet piles with attendant changes in their fracture rate. At fracture surfaces, the initial crystal structure experiences structural phase decomposition which results in dynamic rotations. In fracture and delamination sublayers, the material is fragmented. The effects are more pronounced at Tdef =-196°C.

The mechanisms of propagation of oblique plane harmonic waves through the interface of Voigt and Maxwell viscoelastic media were studied in the context of field theory of defects which describes dislocation continuum dynamics. The defect field waves structure for different displacement wave polarizations was determined. Analytical expressions were derived for the reflection and refraction coefficients of displacement waves and defect field waves propagating in the media. The dependences of Fresnel coefficients on the incidence angle of a primary wave and parameters of the contacting media were analyzed.

Изучены закономерности разрушения агломератов нанолистов оксигидроксида алюминия под действием электрогидравлического разряда. Показана более высокая, чем при ультразвуковом воздействии, эффективность диспергирования электрогидравлическим разрядом. Наибольшее влияние на эффективность разрушения агломератов нанолистов оказывает время выделения энергии, которое определяет интенсивность кавитационных процессов в воде. При выбранных параметрах электрических импульсов измельчения первичных наноструктур не отмечено.