In the work, the dispersion of metal specimens on high-rate heating was studied at the microlevel. The calculations were performed in the framework of the molecular dynamics method with the use of many-body interatomic potentials. It is shown that the electrothermal pulse dispersion has a pronounced stage character. It is pointed out that the processes responsible for evaporation and collision of clusters are much more intense than those of precipitation. Study into the effect of the thermal loading intensity on the dispersion dynamics shows that increasing the heating temperature causes a decrease in the average size of clusters and an increase in their number.

Рассмотрены основные закономерности макроскопической локализации пластической деформации при растяжении металлов и сплавов. Показано, что эффект макролокализации является общим для всех металлов и сплавов в моно- и поликристаллическом состояниях и проявляется на всех стадиях пластического течения независимо от типа кристаллической решетки и механизма деформации (дислокационное скольжение, двойникование). Установлен волновой характер локализации деформации. Обсуждаются такие характеристики волн локализованной деформации, как скорость распространения, длина волны и дисперсия.

Исследована зависимость скорости распространения ультразвуковых волн от действующего напряжения в пластически деформируемых поликристаллических металлах и сплавах. Установлено, что связь между действующим напряжением и скоростью ультразвука линейна, причем эта закономерность характерна для всех исследованных материалов. Предложен способ определения временного сопротивления отрыву материалов (предела прочности) при деформировании в области малых пластических деформаций без разрушения образцов.