A comprehensive structural study has been performed to explore deformation and wear debris formation on friction surfaces of metallic materials. A hierarchy of structural scales of plastic deformation and failure during wear has been established. The nanoscale plays the major role in the hierarchical self-organization of multiscale debris formation processes. On this scale, bifurcational interstitial states arise in zones of local lattice curvature, with plastic distortion and motion of nonequilibrium point defects which determine the nonlinear dynamics of structure formation and wear of surface layers. Nonequilibrium vacancies on lattice sites form microporosity through the coalescence mechanism under plastic distortion. The microporosity is a precursor of meso- and macroscale plastic shearing that defines wear debris formation.

Представлены результаты электронно-микроскопического исследования неравновесных структурных состояний с высокими значениями кривизны и градиентов кривизны кристаллической решетки. формирующихся в объемных наноструктурных металлических материалах, полученных методами интенсивной пластической деформации. Изложена методика их электронно-микроскопической аттестации, исследования внутренних напряжений и градиентов (моментов) этих напряжений, локализованных на субмикронном масштабном уровне. Предложена структурная модель этих состояний как состояний с высокой континуальной плотностью дефектов (дислокаций и дисклинаций) в объеме и на границах зерен.

Проведено электронно-микроскопическое исследование микроструктуры аустенитной стали 02Х17Н14М2 после больших пластических деформаций прокаткой и кручением под давлением в наковальнях Бриджмена. Показано, что основными механизмами формирования дефектной структуры являются механическое двойникование и формирование полос локализации деформации. Обнаружено явление механического двойникования в нанокристаллическом состоянии. Обсуждаются механизмы деформации и формирования наноструктурных состояний.